Bambu Lab PLA-CF

https://www.vertex3d.co/web/image/product.template/1931/image_1920?unique=a56bdee

Product Features
  • Carbon Fiber Texture & Minimized Layer Lines
  • Improved Mechanical Properties
  • Stablized Printing Dimension
  • Comes with Basic Reusable Spool
  • Diameter: 1.75mm +/- 0.03mm

Cautions for Use

  • 0.2 mm Nozzle Not Compatible
  • Stainless Steel Nozzle Not Recommended
  • Dry before Use for the Highest Print Quality
  • AMS Compatible

1.00 Rs. 1.0 PKR 1.00 Rs.

1.00 Rs.

Not Available For Sale

  • Brand
  • Weight
  • Color

This combination does not exist.

Bambu Lab Filament PLA
Brand: BAMBU LAB
Weight: 1Kg

Terms and Conditions
30-day money-back guarantee
Shipping: 2-3 Business Days

Bambu PLA-CF

Bambu PLA-CF is carbon fiber reinforced PLA with improved stiffness and strength. PLA-CF is easy to print and beginner-friendly like regular PLA. It is AMS compatible with low clogging risk at high-speed printing. The prints are in matte finish with almost invisible layer lines, which make it suitable for printing general engineering parts or models requiring a better appearance, like bike frames, brackets and toys.

 

Carbon fiber texture & Minimized layer lines

The addition of carbon fiber gives prints a unique matte finish and effectively hides layer lines, providing a smooth, premium look.



Display of Prints

Bambu PLA-CF could be paired with any PLA series filament to make your prints more colorful and achieve various texture requirements.


 

Improved Mechanical Properties

Bambu PLA-CF exceeds the mechanical properties of PLA Matte in XY Bending Strength, Z Bending Strength, XY Bending Modulus, Z Bending Modulus, XY Impact Strength, and Z Impact Strength by between 20% and 115%, making it more suitable for printing models with higher strength requirements.


Mechanical Properties Comparison

PLA MattePLA-CFImproved %
Tensile Strength - XY/MPa323819%
Tensile Strength - Z/MPa25264%
Bending Strength - XY/MPa538968%
Bending Strength - Z/MPa324953%
Bending Modulus - XY/MPa2360395067%
Bending Modulus - Z/MPa2040226010%
Impact Strength - XY/(kJ/m²)19.223.220%
Impact Strength - Z/(kJ/m²)6.67.818%

*Drying PLA is recommended for humid environments at 55 °C for 8 hours before printing.

 

Minimal effort in support removal

Bambu PLA-CF is designed to support itself. It can be removed more easily compared to regular PLA, and still maintains a smooth support surface.


 

Not prone to clogging in high-speed printing

Bambu PLA-CF is just as easy to print as regular PLA. It can be printed smoothly and consistently at high speed without clogging.



Accessory Compatibility


RecommendedNot Recommended
Build PlateCool Plate, High Temperature Plate or Textured PEI PlateEngineering Plate
HotendHardened Steel Nozzle (0.4 / 0.6 / 0.8 mm)Stainless Steel Nozzle (0.2 / 0.4 mm)
GlueBambu Liquid Glue
Glue Stick


RFID for Intelligent Printing

All printing parameters are embedded in RFID, which can be read through our AMS (Automatic Material System).

Load and print! No more tedious setting steps.

                                               

Recommended Printing Settings
Drying Settings (Blast Drying Oven)55 °C, 8 h
Printing and Keeping Container's Humidity< 20% RH (Sealed, with Desiccant)
Nozzle Temperature210 - 240 °C
Bed Temperature (with Glue)35 - 45 °C
Printing Speed< 200 mm/s
Physical Properties
Density1.22 g/cm³
Vicat Softening Temperature69 °C
Heat Deflection Temperature55 °C
Melting Temperature165 °C
Melt Index3.7 ± 0.6 g/10 min
Mechanical Properties
Tensile Strength38 ± 4 MPa
Breaking Elongation Rate8.4 ± 3.2 %
Bending Modulus3950 ± 190 MPa
Bending Strength89 ± 4 MPa
Impact Strength23.2 ± 3.7 kJ/m²