Product Features
  • Low Moisture Absorption
  • Exceptional Mechanical Properties & Layer Adhesion
  • High Tensile Strength
  • Comes with High Temperature Reusable Spool
  • Diameter: 1.75mm +/- 0.03mm


Cautions for Use

  • 0.2 mm Nozzle Not Compatible
  • Stainless Steel Nozzle Not Recommended
  • Dry Out before Use
  • AMS Compatible
  • Enclosure Printer Required
Note: PAHT-CF is an upgraded version of PA-CF (PA-CF was discontinued).

1.00 Rs. 1.0 PKR 1.00 Rs.

1.00 Rs.

Not Available For Sale

  • Brand
  • Color
  • Weight

This combination does not exist.

Bambu Lab Material
Brand: BAMBU LAB
Color: Black
Weight: 1Kg

Terms and Conditions
30-day money-back guarantee
Shipping: 2-3 Business Days

Bambu PAHT-CF

Bambu PAHT-CF is a composite of PA12 and carbon fiber. Inheriting the advantages of low water absorption from PA12 and high-performance carbon fiber, Bambu PAHT-CF offers excellent mechanical and thermal properties that can be maintained well even when the prints get wet. Higher Z adhesion layers and flexibility make it ideal for creating engineering parts such as functional prototypes, machining fixtures, injection molds, jigs, and low-volume production parts.

 

Low Water Absorption

With a 50% lower water absorption rate compared to normal PA-CF,

Bambu PAHT-CF maintains excellent mechanical properties and dimensional stability even when exposed to high humidity.


Deflection from Dry to Wet

 

Mechanical Properties Comparison

Normal PA-CFPAHT-CF
Saturated Water Absorption Rate/% ( 25 °C, 55% RH )1.700.88
Bending Strength - XY/MPa (Dry)128125
Bending Strength - XY/MPa (Wet)76115
Bending Strength - Z/MPa (Dry)4861
Bending Strength - Z/MPa (Wet)3449
Bending Modulus - XY/MPa (Dry)44204230
Bending Modulus - XY/MPa (Wet)22103640
Bending Modulus - Z/MPa (Dry)14701820
Bending Modulus - Z/MPa (Wet)7701480
Decline rate of mechanical properties after absorbing water/%40%-45%12%-18%

*Both PA-CF and PAHT-CF need to be dried at 80 °C for 12 hours before printing.


Exceptional Z-bonding

Bambu PAHT-CF shows much higher adhesion in Z layers compared to normal PA-CF,

bringing it the ability to withstand high levels of impact or stress without breaking or deforming.



Z-layer Performance

Normal PA-CFPAHT-CFImproved %
Bending Strength - Z/MPa486127%
Bending Modulus - Z/MPa1470182024%
Impact Strength - Z/(kJ/m²)5.713.3133%

*Both PA-CF and PAHT-CF need to be dried at 80 °C for 12 hours before printing.

High tensile strength

Bambu PAHT-CF is designed to meet the demands of various industrial and engineering applications where high strength and durability are required.

Designed for high-temperature resistance

The heat deflection temperature of Bambu PAHT-CF is up to 194℃ (0.45MPa)*, making it useful in applications where the printed parts may be exposed to high temperatures without deforming or losing their strength.

 

Reusable spool

Bambu PAHT-CF comes with a high-temperature resistant spool, which is not prone to deformation in the drying process. Continuing our concept of reducing plastic waste, the spool can also be reused with other Bambu refills.

Accessory Compatibility

RecommendedNot Recommended
Build PlateHigh Temperature Plate Engineering PlateCool Plate
HotendHotend with Hardened Steel Nozzle (0.6 mm, 0.4 mm, 0.8 mm)*Hotend with Stainless Steel Nozzle (all size)
Hotend with Hardened Steel Nozzle (0.2 mm)
GlueGlue StickLiquid Glue

*As the nozzle size increases, the probability of clogging decreases, but the print quality also decreases. Therefore, it is recommended to use a 0.6 mm Hardened Steel nozzle to avoid clogging while maintaining optimal print quality.


RFID for Intelligent Printing

All printing parameters are embedded in RFID, which can be read through our AMS (Automatic Material System). Load and print! No more tedious setting steps. 

                                      


Parameters Comparison


PET-CFPAHT-CF
CompositionPET, carbon fiberPA 12 and other long-chain PA, carbon fiber
Hotend CompatibilityHardened Steel 0.6 (recommended), 0.4, 0.8 mm
Build Plate CompatibilityEngineering Plate, High Temperature Plate, Textured PEI Plate
GlueGlue Stick / Liquid GlueGlue Stick
AMS CompatibilityNOYES
Print Speed< 100 mm/s< 100 mm/s
Toughness (Impact Strength - XY)36.0 kJ/m²57.5 kJ/m²
Strength (Bending Strength - XY)131 MPa125 MPa
Stiffness (Bending Modulus - XY)5320 MPa4230 MPa
Layer Adhesion (Impact Strength - Z)4.5 kJ/m²13.3 kJ/m²
Heat Resistant(HDT, 0.45 MPa)205 °C194 °C
Saturated Water Absorption Rate / % (25 °C,55% RH)0.370.88


Recommended Printing Settings
Drying Settings (Blast Drying Oven)80 °C, 8 - 12 h
Printing and Keeping Container's Humidity< 20% RH (Sealed, with Desiccant)
Nozzle Temperature260 - 290 °C
Bed Temperature (with Glue)80 - 100 °C
Printing Speed< 100 mm/s
Physical Properties
Density1.06 g/cm³
Vicat Softening Temperature220 °C
Heat Deflection Temperature194 °C
Melting Temperature225 °C
Melt Index14.4 ± 2.0 g/10 min
Mechanical Properties
Tensile Strength92 ± 7 MPa
Breaking Elongation Rate8.4 ± 1.8 %
Bending Modulus4230 ± 210 MPa
Bending Strength125 ± 7 MPa
Impact Strength57.5 ± 3.4 kJ/m²